Abstract
WC-Co reinforced C276 alloy composite coatings are fabricated on Q235 steel by laser melting deposition. The microstructure, hardness, wear performance, and electrochemical corrosion behavior of composite coating are studied. The results show that WC-Co particles are mostly uniformly distributed in the coating and provide favorable conditions for heterogeneous nucleation. The microstructure of C276/WC-Co composite coatings is composed of γ-Ni solid solution dendrites and MoNi solid solution eutectics. The WC-Co particles can effectively improve the hardness and wear resistance of C276 alloy. The average hardness of the composite coating containing 10-wt% WC-Co (447 HV0.2) are 1.26 times higher than that of the C276 alloy (356 HV0.2). The wear rate of composite coating containing 10-wt% WC-Co (6.95 × 10−3 mg/m) is just 3.5% of that of C276 coating (196.23 × 10−3 mg/m). However, comparing with Hastelloy C276, the corrosion resistance of C276/WC-Co composite coating decreases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.