Abstract
Several rare earth elements (Sc, La, Pr, Sm, Gd, Dy, Er, and Yb) were evaluated to develop a sintering additive for transparent γ-AlON. After adding 0.2 wt. % of each of the rare earth additives to the α-Al2O3 and AlN starting material, hot pressing was performed at 1850 °C for 1 h under 20 MPa as a screening test, whereby the γ-AlON with Pr-nitrate showed the highest transmittance of 60.4 % at 632 nm. Two-step pressureless sintering was conducted as a separate test for the same starting material after adjusting the amount of Pr-nitrate to 0, 0.1, or 0.2 wt. % to enhance transmittance. The γ-AlON with 0.1 wt. % Pr-nitrate showed the highest transmittance of 80.36 % after 1st and 2nd sintering steps at 1610 and 1940 °C, respectively, indicating that Pr can be an alternative sintering additive to conventional Y2O3, MgO, and La2O3 for the fabrication of transparent γ-AlON.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.