Abstract
The purpose of this study was to evaluate the effect of the various light curing units (plasma arc, halogen and light-emitting diodes) and irradiation methods (one-step, two-step and pulse) using different light energy densities on the leachability of unreacted monomers (Bis-GMA and UDMA) and the surface hardness of a composite resin (Z250, 3M). Leachability of the specimens immersed for 7 days in ethanol was analysed by HPLC. Vicker's hardness number (VHN) was measured immediately after curing (IC) and after immersion in ethanol for 7 days. Various irradiation methods with three curing units resulted in differences in the amount of leached monomers and VHN of IC when light energy density was lower than 17.0 J cm(-2) (P = 0.05). However, regardless of curing units and irradiation methods, these results were not different when the time or light energy density increased. When similar light energy density was irradiated (15.6-17.7 J cm(-2)), the efficiency of irradiation methods was different by the following order: one-step > or = two-step > pulse. These results suggest that the amount of leached monomers and VHN were influenced by forming polymer structure in activation and initiation stages of polymerization process with different light source energies and curing times.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.