Abstract
Vacuum ultraviolet (VUV) photoemission spectroscopy is utilized to investigate the distribution of trapped charges within the bandgap of low dielectric constant (low-k) organosilicate (SiCOH) materials. It was found that trapped charges are continuously distributed within the bandgap of porous SiCOH and the center of the trapped states is 1.3 eV above the valence band of the tested sample. By comparing photoemission spectroscopic results before and after VUV exposure, VUV irradiation with photon energies between 7.6 and 8.9 eV was found to deplete trapped charge while UV exposure with photon energies less than 6.0 eV induces more trapped charges in tested samples. Current-Voltage (IV) characteristics results show that the reliability of dielectrics is improved after VUV irradiation with photon energies between 7.6 and 8.9 eV, while UV exposure results in an increased level of leakage current and a decreased breakdown voltage, both of which are harmful to the reliability of the dielectric. This work shows that VUV irradiation holds the potential to substitute for UV curing in microelectronic processing to improve the reliability of low-k dielectrics by mitigating the leakage currents and trapped charges induced by UV irradiation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.