Abstract
Abstract Goal of the present research was to investigate the influence of V2O5 additive on the structure and dielectric properties of BiNbO4 ceramics. To fabricate BiNbO4 ceramics with V2O5 added the solid state reaction route and pressureless sintering was utilized. Thus obtained ceramics was characterized in terms of its microstructure (SEM), chemical composition (EDS), phase composition and crystalline structure (X-ray phase and structural analysis, respectively). Also dielectric properties in both temperature and frequency domains were investigated. The impedance spectroscopy was utilized for dielectric characterization and the measurements of complex impedance were performed within the frequency range ν =10Hz-1MHz and temperature range T =RT-550°C. It was found that V2O5 additive changed slightly lattice parameters of BiNbO4 ceramics, decreased porosity of samples and revealled relaxation phenomena within the frequency ranges ν =102-103 Hz and ν =105-106 Hz at temperature T>285°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.