Abstract
The effects of ultrasonic deep rolling (UDR) on the fatigue behavior of pre-corroded 7A52 aluminum alloys were investigated. By means of X-Ray diffraction stress measurements and scanning electron microscopy (SEM), residual stress and fractograph of 7A52 aluminum alloys with and without UDR treatment were analyzed. The results indicated that the UDR produced compressive residual stresses with depth approaching 1mm. UDR treatment can extend the fatigue life of the pre-corroded 7A52 specimens to a large extent, depending on the level of corrosion and UDR parameter. For the slightly corrode specimens, the UDR treatment changed the fatigue crack nucleation site from surface to the transition zone between the compressive residual stresses and tensile stresses, resulted in a much longer fatigue life. For the severely corrode specimens, the crack still nucleated by intergranular cracking, however, due to the compressive residual stresses introduced and the closure of the corrosion pits and corrosion micro-crocks, UDR treatment still improved fatigue performance of the pre-corroded 7A52 aluminum alloy substantially.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.