Abstract
This report described the effects of Ti surface modification with NaOH hydrothermal solution on adhesion strength of HA coating produced by newly developed hydrothermal (DC-HHP) method. 2 kinds of surface layer (containing anatase-type TiO2 or not) were formed on Ti surface by immersing to 5 mol/L NaOH solution before HA coating process. Pull out tests were conducted to obtain an estimate for the adhesion properties of the HA coating. Shear strength of specimens with 5 mol/L NaOH treated at 423 K for 2 hours was estimated in the range of 4.1–5.7 MPa. The enhancement of the HA adhesive properties as well as more than three times values was achieved, in comparison to the specimens without the surface layer (approximate 1.5 MPa). It was demonstrated that 423 K hydrothermal treatment with 5 mol/l NaOH solution on Ti surfaces is significantly effective to enhancing adhesion strength of the HA coating produced by the DC-HHP method.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call