Abstract
The microstructure and mechanical properties of hot-pressed zirconia-toughened alumina (ZTA), fabricated from the ZTA powders containing (Zr, Ti)O2 in Ar gas were investigated. In hot-pressed ZTA, the presence of Ti concentration in the grains of Al2O3 or (Zr, Ti)O2 was analyzed by the energy dispersive spectroscopy (EDS) attached to the analytical electron microscope (AEM) apparatus. Experimental results showed that some Ti ions diffused to the grain boundary and into the Al2O3 grains, thereby enhancing the densification of hot-pressed ZTA. It was possible to retain tetragonal ZrO2 at room temperature in the ZTA specimens containing ≥5.5 mol% TiO2 and hot pressed at 1350 °C for 1 h. The bending strength and toughness of hot-pressed ZTA were enhanced by the addition of TiO2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.