Abstract
Ti- xHf ( x=10%, 20%, 30% and 40%, mass fraction) alloys were prepared by arc melting, and the microstructure was controlled for 24 h at 1 000 °C in argon atmosphere. The formation of nanotube was conducted by anodizing on Ti-Hf alloys in 1.0 mol/L H 3PO 4 electrolytes with small amounts of NaF at room temperature. And then TiN coatings were coated by DC-sputtering on the anodized surface. Microstructures and nanotube morphology of the alloys were examined by field emission scanning electron microscopy(FE-SEM) and X-ray diffractometry(XRD). The corrosion properties of the specimens were examined through potentiodynamic test (potential range from −1 500 to 2 000 mV) in 0.9 % NaCl solution by potentiostat. The microstructure shows the acicular phase and α′ phase with Hf content. The amorphous oxide surface is transformed to crystalline anatase phase. TiN coated nanotube surface has a good corrosion resistance.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call