Abstract
Manganese-doped zinc sulfide (ZnS:Mn) nanoparticles were synthesized by mixing aqueous solutions of zinc nitrate and manganese nitrate with sodium sulfide. The photoluminescence (PL) of ZnS:Mn nanoparticles (NPs) dispersed in the aqueous solution was observed at 590 nm using extinction light 320 nm in wavelength. When the S and Zn ion concentrations were equal (equimolar condition), the Mn content in NPs increased with the molar ratio Mn/Zn in the feed solution. PL intensity and PL quantum efficiency were proportional to the Mn content in NPs. The particle size of ZnS:Mn increased with the time elapsed after preparation, although the Mn content was constant. NP absorbance at 320 nm increased with elapsed time due to increasing NP size so that PL intensity increased because of increasing absorbed light energy. However, the quantum efficiency remained almost constant. When the S ion concentration exceeded the Zn ion concentration (excess S ion condition), the particle size and absorbance at 320 nm increased with elapsed time, exhibiting trends similar to those observed in NPs prepared under the equimolar condition. On the other hand, the quantum efficiency under an excess S ion condition increased with the elapsed time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.