Abstract
ABSTRACTEffects of thermal exposure (TE) on high cycle fatigue (HCF) behaviours in Ni-based superalloy GH4169 have been investigated in this study. GH4169 specimens were thermally exposed at 650°C for 1, 2, 7, 14 and 21 days before fatigue test. These TEs produced eruptions, bulge-like features and pits at surface due to oxidation of carbides/nitrides. Fatigue life was not reduced evidently by TE as compared to the specimens in virgin conditions, indicating the insignificant influence of TE on HCF life. Fracture morphology analysis showed fatigue crack mainly initiated from oxides, crystallographic facets and subsurface inclusions. Although long TE is not necessarily related to crack initiation from oxides, crack initiation from oxides is generally associated with a shorter fatigue life.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.