Abstract
Statement of problemThe properties of dental computer-aided design and computer-aided manufacturing (CAD-CAM) materials vary. Studies regarding the effects of aging on the properties of these materials are lacking. PurposeThe purpose of this in vitro study was to evaluate the changes in the mechanical and surface properties of different CAD-CAM materials after thermocycling and mechanical loading. Material and methodsIn total, 150 bar-shaped specimens (17.0×4.0×2.0 mm) were prepared from feldspathic glass-ceramic (VM; Vitablocs Mark II), lithium disilicate glass-ceramic (EX; IPS e.max CAD), zirconia-reinforced lithium silicate glass-ceramic (CD; Celtra Duo), polymer-infiltrated ceramic network (VE; Vita Enamic), and resin-nanoceramic (CS; Cerasmart). Each type was divided into 2 groups (n=15; each). One group was subjected to thermocycling in distilled water at 5 °C to 55 °C for 6000 cycles and 50 N mechanical loading for 1.2×106 cycles. The other group was stored in 37 °C water for 24 hours. Nanoindentation hardness, Young modulus, and 3-point flexural strength were measured for the analyses of the mechanical properties. Surface roughness, surface microstructure, and elemental composition were measured to analyze the surface characteristics. Statistical analyses were performed with 1-way ANOVA with the Tukey HSD post hoc test, independent samples t test, Kruskal-Wallis test with Bonferroni post hoc test, Mann-Whitney U test, and 2-way ANOVA (α=.05). ResultsBefore and after aging, CS exhibited the lowest hardness (1.20 to 1.04 GPa) and Young modulus (13.76 to 13.48 GPa) values (P<.05). EX exhibited the highest flexural strengths (393.43 to 391.86 MPa), and VM exhibited the lowest (109.98 to 112.73 MPa) values (P<.05). CS exhibited the highest surface roughness (Sa and Sq; 10.60 to 28.82, 14.21 to 38.27 nm) values (P<.05). After aging, the hardness and Young modulus of VM, EX, and VE decreased significantly (P<.001). No significant difference was observed in the flexural strengths of the CAD-CAM materials (P>.05). Significant increases were observed in the surface roughness of all the materials (P<.05), with altered microstructures. Except for the flexural strength, the mechanical properties and surface characteristics of the CAD-CAM materials were significantly affected by the material type after aging. ConclusionsBefore and after aging, resin-nanoceramic exhibited the lowest hardness and Young modulus, and the highest surface roughness. Lithium disilicate glass-ceramic exhibited the highest flexural strength and feldspathic glass-ceramic exhibited the lowest value. After aging, increased surface roughness and microstructure alterations were observed. Significant interactions between aging process and material type were found for the mechanical properties and surface characteristics except for the flexural strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.