Effects of the initial microstructure of Ti–Cu alloys on final nanoporous copper via dealloying

Abstract

A Ti60Cu40 ribbon alloy before and after annealing was dealloyed in 0.03M HF and 0.13M HF solutions for 3.6–43.2ks, and a bi-continuous nanoporous copper (NPC) from tenths of nanometers to hundredths of nanometers was obtained. The as-spun amorphous Ti60Cu40 ribbon alloy has a glass transition temperature of 562K and crystallization temperature of 657K. The as-spun ribbon alloy has an amorphous structure, and that after annealing at 633K has a heterogeneous crystalline structure with coexistence of a particle size of 17nm and amorphous phases. The alloy after annealing at 713K has a completely crystalline structure consisting of dendritic Ti2Cu3 and Ti2Cu intermetallic phases. The phase segregation occurs at higher annealing temperatures. The dealloyed crystalline Ti60Cu40 ribbons exhibits multimodal nanoporous structure, which is corresponding to the initial microstructure. The order in uniformity in NPCs is confirmed to be as follows: amorphous alloys>nanocrystalline alloys>completely crystalline alloys, while their characteristic scale length of nanopores and ligaments differs from region to region where the initial microstructure and chemical composition are different. The diffusivity of Ti2Cu3 phase was lower than that of Ti2Cu phase by a factor of 13 due to their difference in chemical composition and microstructure. The difference in the NPC structure became weak in concentrated HF solution due to the higher diffusion in relatively large scales which might exceed the size of nanocrystalline grains. The final NPCs reflected the initial microstructure of the starting materials.