Abstract

Rotating bending (52.5 Hz) and ultrasonic (20 kHz) fatigue tests were performed on the specimens of a bearing steel, which were quenched and tempered at 150 °C, 300 °C, 450 °C and 600 °C, respectively, to investigate the influence of strength level and loading frequency on the fatigue behavior in very-high-cycle regime. Influences on fatigue resistance of materials, characteristics of S– N curves and transition of crack initiation site were discussed. The specimens with higher strength showed interior fracture mode in very-high-cycle regime and with slight frequency effect, otherwise cracks all initiate from the surface and the fatigue strength was much higher under ultrasonic cycling.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.