Abstract
ABSTRACTThe objective of this work is to initiate the discussion about multiphysics relationships between the molten and solid states of high‐density polyethylene (HDPE). The extrusion and the injection processes are employed to prepare samples, and the experimental procedures, using differential scanning calorimetry, dynamic thermomechanical analysis (DMTA), thermal gravimetric analysis, and rheological measurements, are defined to choose the optimal variables. After different characterizations, the extrusion and injection temperatures of 220 and 230 °C have been chosen. To investigate the viscoelastic behavior of HDPE, the DMTA is used. To perform the high strain rate tensile tests, tensile machine was equipped with a specific furnace. Two temperatures, −20 and 20 °C, with strain rates varying from 0.001 to 100 seconds−1 were used to compare the flow characteristics. Results showed that by increasing the strain rate the molecular mobility of the HDPE chains is decreased. In addition, to the tests at −20 °C, the increase of Young's modulus can be properly observed, under high strain rates. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48778.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.