Abstract
Mode II delamination properties of Vectran stitched composites were investigated, and tabbed end notch flexural specimen testing was used to prevent premature failure. The effects of stitch density and stitch thread thickness were explored, and fibre compaction due to the stitching process was also verified. The results show that, in moderately stitched laminates (low stitch density), the improvement in GIIC was negligible. Crack bridging by the stitch threads at the crack zone were mostly compensated for the effect of fibre compaction, which reduced the GIIC values. Conversely, in densely stitched laminates (high stitch density), GIIC values were improved significantly (2·4 times higher than those of unstitched laminates). The effects of stitch thread thickness appeared to be negligible in moderately stitched laminates. For densely stitched laminates, thicker stitch thread (500 denier) possessed GIIC values that were 45·7% higher than thinner stitch thread (200 denier).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.