Abstract
The accumulation of steel slag and other industrial solid wastes has caused serious environmental pollution and resource waste, and the resource utilization of steel slag is imminent. In this paper, alkali-activated ultra-high-performance concrete (AAM-UHPC) was prepared by replacing ground granulated blast furnace slag (GGBFS) powder with different proportions of steel slag powder, and its workability, mechanical properties, curing condition, microstructure, and pore structure were investigated. The results illustrate that the incorporation of steel slag powder can significantly delay the setting time and improve the flowability of AAM-UHPC, making it possible for engineering applications. The mechanical properties of AAM-UHPC showed a tendency to increase and then decrease with the increase in steel slag dosing and reached their best performance at a 30% dosage of steel slag. The maximum compressive strength and flexural strength are 157.1 MPa and 16.32 Mpa, respectively. High-temperature steam or hot water curing at an early age was beneficial to the strength development of AAM-UHPC, but continuous high-temperature, hot, and humid curing would lead to strength inversion. When the dosage of steel slag is 30%, the average pore diameter of the matrix is only 8.43 nm, and the appropriate steel slag dosage can reduce the heat of hydration and refine the pore size distribution, making the matrix denser.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.