Abstract
The effects of the starting SiC powder (α or β) with the addition of 5.67 wt% AlN–Y2O3–CeO2–MgO additives on the residual porosity and thermal conductivity of fully ceramic microencapsulated (FCM) fuels were investigated. FCM fuels containing ∼41 vol% and ∼37 vol% tristructural isotropic (TRISO) particles could be sintered at 1870 °C using α-SiC and β-SiC powders, respectively, via a pressureless sintering route. The residual porosities of the SiC matrices in the FCM fuels prepared using the α-SiC and β-SiC powders were 1.1% and 2.3%, respectively. The thermal conductivities of FCM pellets with ∼41 vol% and ∼37 vol% TRISO particles (prepared using the α-SiC and β-SiC powders, respectively) were 59 and 41 Wm−1K−1, respectively. The lower porosity and higher thermal conductivity of FCM fuels prepared using the α-SiC powder were attributed to the higher sinterability of the α-SiC powder than that of the β-SiC powder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.