Abstract
ABSTRACTDirectional solidification of Cr-Cr3Si eutectic alloys has been carried out using a high temperature optical floating zone furnace. Uniform and well-aligned lamellar structures were obtained over a fairly wide range of intermediate growth rates but not at very low or very high growth rates where degenerate and cellular structures, respectively, were obtained. The lamellar spacing was found to increase with decreasing solidification rate, in agreement with the Jackson-Hunt theory. In addition, for a fixed growth rate, the lamellar spacing was found to increase with increasing rotation rate. Lamellar structures could also be produced at off-eutectic compositions, but only for a limited range of growth conditions. The Cr-rich lamellae are effective in stopping indention cracks nucleated in the brittle Cr3Si phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.