Abstract
The effects of solid solution temperature on the structures and properties of TC16 titanium alloy bars that made solid solution treatment in 780°C, 800°C, 850°C, 900°C, respectively, the processing time for 30min, then cooled in the air were studied. The results show that during solid solution treatment under 800°C, the alloy structures are the primary ɑ phase and the metastable β phase, while solid solution temperature rise to 800°C, the alloy structures begin to appear ɑ" martensite phase. With the increase of solid solution temperature, the alloy grain grow up somewhat, material tensile strength increases gradually, yield strength firstly decreases and then increases, elongation at break firstly increases and then decreases, percentage reduction of area at break decreases gradually. Solid solution state of TC16 titanium alloy bars are not suitable for cold heading forming, strengthening the titanium alloy must be subsequent artificial aging treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.