Abstract
The effects of Sn content and aging conditions on superelasticity in Ti–Mo–Sn alloys were investigated. Martensitic transformation temperature decreased with an increasing of Sn content. A large superelastic strain of 3.0% was obtained in a solution-treated Ti–5 mol%Mo–5 mol%Sn alloy in the tensile test. The superelasticity in the Ti–5 mol%Mo–5 mol%Sn at room temperature was improved by aging at 873 K for short periods between 180 and 420 s. A specimen aged at 873 K for 300 s exhibited superelasticity with a recovery strain of 3.5% in the tensile test. A recovery strain of 3.0% was consistently achieved in cyclic tensile deformations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.