Abstract
Foam replication method is capable of producing foams with a highly porous structure with adjustable pore dimension, shape and size. In this work, this method has been used to prepare stainless steel 316L foam and sintered at 1200°C, 1250°C and 1300°C in a vacuum furnace. The microstructure and elemental analysis of the sample were examined using scanning electron microscope (SEM) and Energy Dispersive X–Ray (EDX), while the mechanical properties of the samples was determined by using compression test. It was found that the average pore size was in the range of 330µm-350µm. The yield strength and elastic modulus are in the range of 58-66 GPa and 0.46-0.50GPa respectively.