Abstract
A new method to weaken the interfacial bonding and increase the strength of 3D mullite fiber reinforced mullite matrix (Muf/Mu) composites is proposed and tested in this paper. Firstly, Muf/Mu composites were fabricated through sol–gel process with varied sintering temperature. Then, the effects of sintering temperature on mechanical properties of the composites were tested. As sintering temperature was raised from 1000 °C to 1300 °C, the three-point flexural strength of the composites firstly decreased from 66.17 MPa to 41.83 MPa, and then increased to 63.17 MPa. In order to explain the relationship between composite strength and sintering temperature, morphology and structure of the mullite fibers and mullite matrix after the same heat-treatment as in the fabrication conditions of the composites were also investigated. Finally, it is concluded that this strength variation results from the combined effects of matrix densification, interfacial bonding and fiber degradation under different sintering temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.