Abstract

Effects of Sc3+ admixture on luminescence and scintillation properties were studied in Ce3+ - doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films grown by the isothermal liquid phase epitaxy technique. The Ce3+ photoluminescence (PL) was slightly blue shifted with increasing Sc content due to a decrease in crystal field splitting of the Ce3+ 5d levels. In addition, the thermal activation energy of PL quenching, estimated from the temperature dependence of PL decay times, decreased with increasing Sc content. Lu2YAl4ScO12:Ce exhibited the highest light yield (LY) value of 420 photons/MeV at 5.5 MeV α particles along with a fast scintillation decay time constant (τe) of 17.4 ns. At room temperature, the decrease of LY value with increasing Sc content could be attributed to the thermal ionization process.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.