Abstract
Effects of Sc addition on the microstructure and mechanical properties of cast Al-3Li-1.5Cu-0.15Zr alloy were investigated by microscopy methods and tensile tests. With the addition of 0.15wt% Sc, the grain size of studied alloy in as-cast state decreased from 120µm to 30µm and did not grow obviously after two-step solution treatment (32h at 500°C+24h at 560°C). After aging at 175°C for 32h, the elongation (EL) of Sc-containing alloy reached 5.5%, which increased by 83% compared with Al-3Li-1.5Cu-0.15Zr alloy. The key factors for improvement of comprehensive mechanical properties in Al-3Li-1.5Cu-0.15Zr-0.15Sc alloy could be summarized as follows: grain refining, size reduction of δ’ phases and the precipitation of core/double-shell Al3 (Li, Sc, Zr) composite particles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.