Abstract
The microstructure and mechanical properties of aged Mg-5.5Al-1.2Y magnesium alloy with Sb addition are investigated by optical microscope, SEM and X-ray diffraction analyzer. The results show that with proper content of Sb addition,the microstructure of Mg-5.5Al-1.2Y magnesium alloy is refined obviously and high melting point intermetallic compounds Sb3Y5 and Mg3Sb2 are formed. Meanwhile, the β-Mg17Al12 phase is more distributed. With the increase of Sb addition, the mechanical properties of the alloy at room and elevated temperature increase at first, and then decrease. When the content of Sb is up to 0.5%, the values of tensile strength and elongation at room temperature, 150ºC and 175ºC are up to their maxima synchronously, 241MPa /16.84%, 198MPa/20.27.86% and 169MPa/21.21% respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.