Abstract
Mechanical stability of retained austenite and its effect on mechanical properties of high strength TRIP steel were studied by means of OM, SEM, TEM, XRD, and mechanical testing after various heat treatments. Results revealed that the film-type retained austenite located between bainite laths with high carbon content showed gradual martensitic transformation with strain, demonstrating a good TRIP effect. Samples annealed at 800°C and held at 420°C showed an optimum value of strength and ductility product up to 18381.2MPa%. Transformation kinetics of the retained austenite were evaluated through tensile tests and fitted by the function y=0.86-0.86×exp(-Ax). The fitting results were good.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.