Abstract
A novel quenching‐partitioning‐tempering (Q‐P‐T) process is applied to 60Si2Mn spring steel, resulting in multiphase microstructures consisting mainly of retained austenite (RA) and softened martensite (SFM). The influence of multiphase microstructures on the high‐cycle fatigue behavior of Q‐P‐T and traditional quenching and tempering (Q&T) spring steels are investigated under rotating–bending and tension–tension loading. The results indicate that the fatigue strength of Q‐P‐T spring steel with RA, SFM, and lower quenching stress increases by 23.9 and 14.4% under cyclic rotating–bending and tension–tension loadings, respectively, compared with that of Q&T spring steel. Under both loading modes, the fatigue crack of the Q‐P‐T spring steel is mainly initiated from the interface between the martensitic matrix and inclusions or carbides. In contrast, the fatigue crack of the Q&T spring steel is mainly initiated from the plastic area around the martensitic matrix rather than inclusions. The RA, SFM, and lower quenching stress of the Q‐P‐T spring steel are conducive to the formation of dimples and tear ridges in the crack propagation and ultimate failure areas, whereas the inadequate SFM and higher quenching stress of the Q&T spring steel are prone to the formation of quasi‐cleavage facets and secondary cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.