Abstract
AbstractThe tensile fatigue behavior of unnotched injection molded polysulfone specimens has been investigated. The effects of orientation and residual stress were studied by comparing asmolded specimens with annealed or annealed and quenched specimens with a known residual stress pattern. The treatments are shown to have differing effects at high stresses, where failure is by shear yielding and necking, and at intermediate stresses, where failure is by fatigue crack propagation. The geometries of fatigue cracks are described for each case. An attempt is made to separate the effects of crack and craze initiation from crack propagation, and cyclic loading from cumulative time under load.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.