Abstract
Al2O3/SiC ceramic composites with different SiC contents have been prepared by powder metallurgy at 1600 °C for 120 min at 30 MPa pressure. The effect of second phase particles on the microstructure and mechanical properties of composites have been studied. The results show that SiC particle has a significant impact on the matrix subjected to residual stress, and on the microstructure of the composites as well. The average grain size of alumina matrix decreases as the SiC particle content increases. Simultaneously, it has been found that the mechanical properties of the material are significantly enhanced in comparison with monolithic Al2O3. The highest strength and toughness are obtained when the SiC content is 15 vol%, and the values are 1237 MPa and 5.68 MPa m1/2, respectively. The mechanisms of strengthening and toughening have been discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.