Abstract
PurposeThe purpose of this paper is to investigate the effects of zinc (Zn) nanoparticles on the interfacial intermetallic compounds (IMCs) between Sn‐3.8Ag‐0.7Cu (SAC) solder and Cu substrate during multiple reflow.Design/methodology/approachThe nanocomposite solders were prepared by manually mixing of SAC solder paste with varying amounts of Zn nanoparticles. The solder pastes were reflowed on a hotplate at 250°C for 45 s for up to six times. The actual Zn content after reflow was analyzed by inductively coupled plasma‐optical emission spectroscopy (ICP‐OES). The wetting behavior of the solders was characterized by analyzing the contact angles and spreading rates according to the Japanese Industrial Standard (JIS 23198‐3, 2003). The interfacial microstructure of the solder joints were investigated by field emission scanning electron microscope (FESEM) and energy dispersive X‐ray spectroscopy (EDAX).FindingsIt was found that upon the addition of 0.3 wt% Zn nanoparticles to the SAC solder, the growth of interfacial intermetallic compound (IMC) layers was retarded to a minimum value. Excessive amount of Zn nanoparticles (0.8 wt%) induced an additional IMC layer (Cu5Zn8) which increased the total IMC thickness and raising the reliability issue.Originality/valueIt is concluded that Zn nanoparticles undergo melting/reaction during reflow and impart their effect on the IMCs through alloying effects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.