Abstract
AbstractRapid thermal annealing (RTA) was applied to anneal polycrystalline CdTe thin films evaporated on CdS/ITO substrate and the effects of rapid thermal annealing temperatures and gas environments were studied. X-ray diffractometer (XRD), X-ray photoelectron spectroscopy(XPS), energy dispersive X-ray spectroscopy(EDX), cross-sectional transmission microscopy(TEM), and micro-EDX in TEM were used to characterize physical and chemical properties of rapid thermal annealed CdTe thin films. Complete CdTe/CdS photovoltaic cells were fabricated and I-V characteristics of these cells were measured under the illumination. Results showed that the bulk composition of CdTe remained stoichiometric to 550°C in the air environment and surface composition became Cd-rich. Cross-sectional TEM and micro-EDX showed columnar grains and micro-twins remained even after RTA, however, sulfur content in rapid thermal annealed CdTe caused by sulfur diffusion from CdS during the annealing was much smaller than that by furnace annealing. Among the investigated RTA temperatures and gas environments, the cell made with CdTe annealed at 550°C in the air showed the best solar energy conversion efficiency.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.