Abstract
AbstractIn an effort to investigate the stability of the surface and hetero-interface of AlGaN/GaN HEMTs during high temperature device processing steps, AlGaN/GaN HEMT samples were subjected to temperatures from 650°C to 1150°C for a period of 30 seconds prior to processing. Hall and photoluminescence measurements were performed on samples before and after temperature stressing. The samples annealed at 700°C and 1150°C were then processed, and electrical parametric data were collected during and after processing. Large increases in HEMT Schottky gate diode reverse leakage current are observed at higher pre-process annealing temperatures, while the low-field mobility decreases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.