Abstract
The dynamics of electron transfer at the dye-titania and titania-electrolyte interfaces is investigated in two post-sensitization processes: (i) atomic layer deposition of blocking alumina coating and (ii) hierarchical molecular multicapping. To measure the electron transfer dynamics, time-resolved spectroscopic methods (femtosecond transient absorption on the time scale from femtoseconds to nanoseconds and electrochemical impedance spectroscopy on the time scale from milliseconds to seconds) are applied to the complete dye-sensitized solar cells with cobalt-based electrolyte and champion ADEKA-1 dye (with silyl-anchor unit) or its popular carboxyl-anchor analogue, MK-2 dye. Both molecular capping and alumina blocking layers slow down the electron injection process (the average rate constant decreases from 1.1 ps-1 to 0.4 ps-1) and partial sub-nanosecond back electron transfer from titania to the dye (from ca. 10 ns-1 to 5 ns-1). Very small alumina layers (of 0.1 nm thickness) have the highest impact on reducing the rate constants of these electron transfer processes, and for the thicknesses greater than 0.3 nm the rate constants hardly change. In contrast, the electron recombination between titania and electrolyte, occurring on the millisecond time scale, starts to be significantly suppressed for the blocking layers of 0.3 nm or more in thickness (up to ca. 20 times for 0.5 nm thickness with respect to that for untreated sample), improving open circuit voltage and fill factor of the cells. The amplitude of the relative photocurrent (short circuit current per number of absorbed photons) is found to depend almost exclusively on the ultrafast and fast processes taking place in the first nanoseconds after dye excitation. The positive impact of coadsorbents on the solar cells performance for both ADEKA-1 and MK-2 is also studied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.