Effects of polymeric matrix on accelerated UV weathering properties of wood-plastic composites

Abstract

Abstract The purpose of this work is to compare the weathering properties of different types of wood-plastic composites (WPCs) based on high-density polyethylene (HDPE), recycled high-density polyethylene (rHDPE-I and rHDPE-II), low-density polyethylene (LDPE), polypropylene (PP), recycled polypropylene (rPP), polystyrene (PS), and recycled polystyrene (rPS). The modulus of rupture (MOR) and modulus of elasticity (MOE) of all WPCs decreased with increasing exposure time of weathering. Of these, the rHDPE-II-based composite exhibited the highest MOR and MOE retention ratios after 2000 h of accelerated ultraviolet (UV) weathering, while the PS-based WPC had the lowest values. In addition, the carbonyl index difference (CID) of various WPCs increased significantly as a function of exposure time. Among them, the PS-based WPCs exhibited the most severe degradation due to photo-oxidation on the surface, while the degradation of PE-based WPCs was the mildest. These results are consistent with the change in the surface cracking and flexural properties of the composites. The PS-based WPCs also exhibited higher moisture diffusion coefficients. The mechanical behavior of WPCs after weathering is influenced by a combination of factors, such as surface oxidation, morphology changes, and moisture absorption.