Abstract
Calcium oxide (CaO) is an important construction material, used as expansive agent, alkaline activator, and repairing material for historical structures. In this study, the dissolution and subsequent hydration of CaO, with or without the polycarboxylate ether (PCE)-based superplasticizer, were investigated to elucidate the complex crystallization process of calcium hydroxide (Ca(OH)2). On contact with pure water, CaO particles began to hydrate within a few minutes, while releasing a significant amount of heat. Adding superplasticizer slowed such rapid heat evolution by forming a dormant period and significantly affected the crystallinity of the hydration product. The dormant period was controllable by the amount of added superplasticizer. Moreover, as a result of early nucleation of Ca(OH)2, the formation of 10–100-nm spherical nanoparticles was observed via an in-situ transmission electron microscope, which completely differed from the final crystal shape of the hydration product.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.