Abstract
Pb(Zn1/3Ni2/3)c(Ni1/3Nb2/3)a(ZrxTiy)bO3 (PZN–PNN–PZT, the ratios of PNN/PZT a/b were 0.88, 1 and 1.136) piezoelectric ceramics were prepared by a traditional solid-state reaction method. The effects of PNN/PZT ratio on phase structure, microstructure and electric properties as well as the relaxation behaviors of PZN–PNN–PZT ceramics were investigated. The XRD patterns showed that all ceramics samples had a pure perovskite phase structure. Meanwhile, it was found that the phase structure undergoes a tetragonal, tetragonal-rhombohedral to rhombohedral transition as ratios of PNN/PZT increased. With the increasing of a/b from 0.88 to 1.136, the dielectric constant and diffusive phase coefficient decreases, it was indicated that relaxation behaviors also decreased. When ceramics with a/b was 1.136, the dielectric relaxation γ reached the minimum and electrical properties were poor. The electric properties of ceramics with a/b was 1.00 have an excellent properties, it was indicated that ceramics reached an optimization at the MPB structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.