Abstract
In this study, the in situ Al3Ti/2024Al composites were successfully fabricated by direct melt reaction method and subjected to forging and friction stir processing (FSP) to achieve superplasticity. Then, the microstructure and superplastic tensile behavior of the composites were investigated. The results show that the reinforcement particles are broken and grains are fine after plastic processing. Particularly, the size of reinforcement particles ranges from 0.2 μm to 5 μm and the average size of fine equiaxed grains is 5 μm after FSP processing. And the superplasticity of the composites was improved apparently. The maximum elongation of 642% was obtained at 0.15 s−1 and 510 °C for the FSP specimen, with a strain rate sensitive parameter (m) of 0.58, indicating the FSP specimen has obtained excellent high strain rate superplasticity. The strain rate sensitivity parameter, m, ranges from 0.23 to 0.58, and the activation energy was calculated to be 135.24 kJ mol−1. All results indicated that the main superplastic deformation mechanism was grain boundary sliding (GBS) for the FSP Al3Ti/2024Al composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.