Abstract
In this paper, the effect of neutron irradiation on sapphire single crystal with fast neutron of 1.0×10 18 and 1.0×10 19 neutrons/cm 2 has been investigated along with the effect of annealing temperature. It is found that the colorless transparent sapphire single crystals were turned yellow after 10 MeV fast neutron irradiation at room temperature. There are peaks at 206, 230, 258, 305, 358 and 452 nm after neutron irradiation. And the intensity of optical absorption bands decrease with wavelength and annealing temperature. A new absorption peak at 452 nm was found after isothermal annealing at 400 °C for 10 min, which was ascribed to F 2 + color center. Because of the recombination of interstitial ions and vacancies, color centers were almost removed after annealing at 1000 °C. The TL peaks were found to shift to higher temperature after neutron irradiation. And a higher fluence of the neutron irradiation would result in deep traps revealed as the new TL peaks at 176 and 227 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.