Effects of Neutron, Ion and Proton Irradiation on Nano-Indentation Hardness of RPV Steels

Abstract

The irradiation embrittlement damage of reactor pressure vessel (RPV) steel is one of its primary failure mechanisms. In this work, neutron, ion and proton irradiation experiments were carried on the same commercial RPV steels with the same irradiation fluence under the same temperature of 292°C. Then the nano-indentation hardness tests were performed on the RPV steel before and after irradiation. The results show that the irradiation hardening effects are observed by means of nano-indentation technique under the above three irradiations, and the hardening features are basically the same. While the max variation and increase rate are obviously different between those irradiations. It is found that the main reason of the above differences are caused by different energies of irradiation energetic particles, resulting in different types and quantities of defects. The conclusions in this paper are helpful to select and compare different irradiation experiments to the research of RPV steels irradiation embrittlement damage.