Abstract
The influences of Niobium doping on the glass-forming ability (GFA) and magnetization properties of Nd–Fe–B–Nb alloys were investigated. It is found that the GFA of Nd–Fe–B–Nb alloys are improved by the Nb addition. It is also revealed that the GFA of the samples increases with the Nb content. Rapidly solidified Nd4.5Fe77−xNbxB18.5 (x = 0, 0.25, 0.5, 0.75, 1) nanocomposite strip flakes were successfully prepared by using strip casting technique with a higher production efficiency and a lower cooling rate compared to melt spinning method. The coercivity of nanocomposite Nd–Fe–B–Nb alloy strip flakes can be dramatically enhanced by 0.5 at. % Nb addition, attributing to grain refinement. The best magnetic properties with Hcj = 278.9 kA/m, (BH)max = 41.06 kJ/m3 have been obtained in Nd4.5Fe76.5Nb0.5B18.5 nanocomposite strip flake, which can be used for bonded magnets. The recoil loss of Nd4.5Fe76.5Nb0.5B18.5 alloy is also reduced by the Nb addition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.