Abstract
BackgroundInadequate retention and gradual debonding of intracanal post from root dentin is a major cause of failure of endodontically treated teeth restored with fiber post.Main bodyThis study aimed to assess the effect of surface treatment of quartz fiber posts with different powers and motion directions of Er,Cr:YSGG laser on their pull-out bond strength to root dentin in endodontically treated premolar teeth. In this study, 105 fiber posts were divided into 7 groups according to their surface treatment with different powers of Er,Cr:YSGG laser at 2780 nm wavelength, 20 Hz frequency and 150 μs pulse duration in circumferential (C) or longitudinal (L) motion directions: Control group (no treatment), 0.5 W laser in longitudinally (L0.5), 1.0 W laser in longitudinally (L1), 1.5 W laser in longitudinally (L1.5), 0.5 W laser in circumferentially (C0.5), 1.0 W laser in circumferentially (C1) and 1.5 W laser in circumferentially (C1.5). After cementation, pull-out bond strength was measured in Newton (N). Each sample was inspected under a stereomicroscope at × 25 magnification to determine the mode of failure. Two samples of each group were inspected under a scanning electron microscope (SEM). Data were analyzed using two-way ANOVA and Tukey’s test with significant level of 0.05. The pull-out bond strength of 0.5 W groups had significant differences with the control group (P = 0.009). The bond strength of 1.0 W and 1.5 W groups were not significantly different (P = 0.630) but were higher than the control and 0.5 W groups (P < 0.001). Motion direction of laser irradiation had no significant effect on the bond strength (P = 0.384). The interaction effect of power and motion direction of laser irradiation had no significant effect on the bond strength (P = 0.092).ConclusionFiber posts treated with 0.5, 1.0 and 1.5 W Er,Cr:YSGG laser showed higher bond strength to dentin compared to posts with no surface treatment. However, the motion directions of laser irradiation had no significant effect on the bond strength. In order to minimize damage to post surface and achieving maximum bond strength, longitudinal surface treatment of posts with 1.0 W power of Er,Cr:YSGG laser is recommended.
Highlights
IntroductionInadequate retention and gradual debonding of intracanal post from root dentin is a major cause of failure of endodontically treated teeth restored with fiber post
Inadequate retention and gradual debonding of intracanal post from root dentin is a major cause of failure of endodontically treated teeth restored with fiber post.Main body: This study aimed to assess the effect of surface treatment of quartz fiber posts with different powers and motion directions of Er,Cr:YSGG laser on their pull-out bond strength to root dentin in endodontically treated premolar teeth
Fiber posts treated with 0.5, 1.0 and 1.5 W Er,Cr:YSGG laser showed higher bond strength to dentin compared to posts with no surface treatment
Summary
Inadequate retention and gradual debonding of intracanal post from root dentin is a major cause of failure of endodontically treated teeth restored with fiber post. Main body: This study aimed to assess the effect of surface treatment of quartz fiber posts with different powers and motion directions of Er,Cr:YSGG laser on their pull-out bond strength to root dentin in endodontically treated premolar teeth. The interaction effect of power and motion direction of laser irradiation had no significant effect on the bond strength (P = 0.092). To increase the retention of restoration, metal or fiber posts are used in the root canal of endodontically treated teeth. Surface treatment of fiber posts with hydrogen peroxide significantly increases their shear bond strength [3, 4]
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.