Abstract
The corrosion and hydrogen-induced cracking (HIC) resistance as well as hydrogen permeation behavior of two API 5L X65 steels with different amounts of Mn and microalloying elements were compared. The corrosion behavior of both steels, evaluated using electrochemical impedance spectroscopy and polarization curves in solution A of NACE TM0284-16 standard with and without H2S saturation (sour medium), showed no relevant differences in each medium, which can be ascribed to their similar microstructures; however, the corrosion resistance of both steels was lower in the sour medium. The investigation of resistance to hydrogen-induced failures disclosed better performance for the low Mn steel. This was confirmed using a harsher HIC test performed in an HCl acidified sour medium and was ascribed to the presence of Nb carbides nanoprecipitates, as revealed by the scanning transmission electron microsccopy analysis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.