Abstract
The corrosion behaviors and mechanisms of plasma-sprayed X1-Gd2SiO5 and X2-RE2SiO5 (RE=Y, Er) environmental barrier coatings against CMAS melts at 1400 °C were explored. Results showed that the RE2SiO5 coatings dissolved into CMAS melts and formed a continuous dense layer of apatite phase at the interface, while garnet phase was only found in the X2-Er2SiO5 coating. The recession of RE2SiO5 was related to its microstructure and RE ionic radius. The RE2SiO5 with X2 phase and smaller RE ionic radius exhibited better corrosion resistance due to its more stable crystal structure, lower reactivity with CMAS and easier to form garnet phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.