Abstract
The heterogeneous microstructure of solder could be obtained when cooling rate of the solder joint was not even, which would affect the corrosion behavior of solder during service. The ambient temperature would also affect the corrosion behavior of solder joint. In this paper, the effects of microstructure and temperature on the corrosion behavior of Sn–3.0Ag–0.5Cu (SAC305) lead-free solder were investigated. The various microstructures of SAC305 lead-free solder were obtained by cooling specimens in air and furnace. Compared to the fine-fibrous Ag3Sn phase inside the commercial SAC305 solder, platelet-like Ag3Sn formed as cooling speed decreasing. The polarization behavior of SAC305 solders in 3.5 wt.% NaCl solution was not significantly affected by various microstructures, but sensitive to temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.