Abstract
The effects of MgO addition on properties such as density, firing shrinkage, microstructure, Vickers hardness, and fracture toughness of ZTA–CeO2 ceramics composites were investigated. The amount of CeO2 used in the experiment was fixed at 5.0wt% while the MgO addition was varied from 0wt% to 2.0wt%. Each composition was weighed, mixed, and pressed using hydraulic press under 300MPa into 13mm pellets. The pellets were sintered at 1600°C for 4h under pressureless condition. Vickers hardness and fracture toughness of the sintered samples were measured using the Vickers indentation method. Based on the SEM microstructures, elongated secondary phase, i.e. MgAl11CeO19, started to occur at 0.5wt% MgO. This elongated phase was responsible for the increase in fracture toughness of the ceramic composites. Similarly, the addition of more than 0.5wt% MgO produced another secondary phase (MgAl2O4), as detected by XRD. This phase was shown to have low intrinsic fracture toughness. Therefore, the sample with 0.5wt% MgO showed the optimum properties with the highest fracture toughness (9.14MPam) and Vickers hardness (1591HV) values.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.