Abstract
MgxZn1-xO:Al ceramics with low resistivity using ZnO, MgO and Al2O3 nano-powders as raw materials were obtained by unpressurized sintering. The influence of Mg content on structure and electric properties of MgxZn1-xO:Al ceramics were studied. The results indicate that there is a single phase of wurtzite structure of ZnO in MgxZn1-xO:Al ceramics at x ≤ 0.3, and when the value of x was 0.3, phase separation was observed. The grains become smaller and more homogeneous with increasing Mg content to above 0.3. The resistivity of MgxZn1-xO:Al ceramics obviously increases with increasing Mg concentration due to the decrease of the carrier concentration and the mobility deriving from the decrease of Al-doping efficiency. The electrical conduction of MgxZn1-xO:Al ceramics can be markedly improved by increasing the Al-doping level and the lowest resistivity of 8.3×10-4Ω•cm can be obtained when Mg/(Mg+Zn)=0.2 and Al/(Mg+Zn+Al)=0.03.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call