Abstract
The Mg2SiO4-MgTiO3-CaTiO3 composite dielectric ceramics with different Mg2SiO4 addition amounts were prepared by solid state reaction method. The effects of Mg2SiO4 addition amounts on the microstructure and dielectric properties as well as sintering temperature of xMg2SiO4-(0.95-x)MgTiO3-0.05CaTiO3 (abbreviated as xMSTC, 0.25≦x≦0.75) composite ceramics were investigated. The results indicated that the sintering temperature of MgTiO3-CaTiO3 based ceramics with Mg2SiO4 addition could be lowered effectively to 1320~1340°C, and the dielectric constant decreased and dielectric loss increased gradually with the increase of Mg2SiO4 content. The 0.45MSTC ceramics containing 45 wt% Mg2SiO4 and sintered at 1340°C showed desirable dielectric properties with dielectric constant εr=13.3，dielectric loss tanδ=4.5×10-4 and temperature coefficient of relative permittivity τε =10 ppm/°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.