Abstract

Abstract Urea-melamine-formaldehyde (UMF) resins were synthesized and used for manufacturing medium-density fiberboard (MDF). As melamine content was increased at the same formaldehyde/urea (F/U) molar ratio, the solids content of the resin increased. Physical properties and storage stability of the resins tended to improve slightly when the final pH of resin was 8.5 compared with 7.5 and 9.5. At the same F/U molar ratio, free formaldehyde content and gel time of the resins decreased as melamine content increased. Chemical structures of the resins were proposed from the results of 13C nuclear magnetic resonance and Fourier transform infrared analyses. Formaldehyde emissions of MDF prepared with UMF resins with the same F/U molar ratio decreased as melamine content of resin was increased. MDF fabricated with UMF resin showed slightly better resistance against decay fungi and termites compared with MDF fabricated with urea-formaldehyde (UF) resin. Other physical properties of MDF fabricated with UMF resin w...

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call