Abstract
The effects of Mn and Fe contents on the mechanical properties of aluminum-based A206 alloys were investigated quantitatively. Results showed that the addition of Fe caused a loss in both ductility and yield strength. Further addition of Mn could recover the ductility, but it caused a further loss in yield strength. In low-Mn alloys (0.29 wt% Mn) the primary constituent was the needle shape of Cu2FeAl7. Upon further addition of Mn, the Chinese script configuration of Mn-bearing particles formed instead. The Cu2Mn3Al20 particles formed in high-Mn alloys during solution treatment and resulted in grain-growth inhibition. The needle, Mn-bearing, and Cu2Mn3Al20 particles caused the solid solution level of copper in the matrix to decrease; meanwhile, increasing the Mn solution level retarded the precipitation of the strengthening phase. Differential scanning calorimetry analyses showed the kinetics and amount of decrease in θ′ phase precipitation when the contents of Fe and/or Mn were increased. The smaller grain size induced by the Cu2Mn3Al20 particles and the θ′ phase were the factors that determined the hardness of A206 alloys under as-quenched and T7-treated conditions, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.